Post-exposure testing of powerformer furnace tubes

Electron beam welding can be used in the fabrication of specimens where limited material is available
EB welded specimen
Some 2.25%Cr-1%Mo furnace tubes had been removed from service during a modification of the furnace layout after prolonged service (more than the design life of 100,000hr).

Calculation suggested that the tubes were approaching the end of their available lives, based upon the standard creep rupture data available. These tubes were made available to TWI for Remaining Life Assessment (RLA) by post-exposure creep testing. The wall thickness of the tubes was insufficient for the fabrication of conventional creep specimens and rods of test material were electron beam welded on to sections of matching composition for the larger diameter threaded ends to the specimens. A small-scale programme of accelerated stress rupture tests was performed and it was found that under the design conditions of temperature and stress there was still a very significant creep life remaining and retubing could be postponed for several years.

Copyright © 2001, TWI Ltd

Information and advice from TWI and its partners are provided in good faith and based, where appropriate, on the best engineering knowledge available at the time and incorporated into TWI's website in accordance with TWI's ISO 9001:2000 accredited status. No warranty expressed or implied is given regarding the results or effects of applying information or advice obtained from the website, nor is any responsibility accepted for any consequential loss or damage.